직접 결합 마그네시아 크롬 벽돌은 SiO2가있는 고순도 소결 마그네시아 및 크롬 농축액으로 만들어집니다.< 2%="" as="" raw="" materials="" through="" high-temperature="" sintering.="" the="" direct="" bonding="" degree="" of="" the="" product="" increases="" with="" the="" reduction="" of="" sio2="" content="" and="" the="" increase="" of="" sintering="" temperature.="" the="" formation="" of="" direct="" bonding="" is="" a="" process="" of="" dissolution="" precipitation.="" increasing="" the="" content="" of="" fine="" powder="" of="" chromium="" concentrate="" is="" conducive="" to="" the="" formation="" of="" direct="" bonding.="" in="" the="" presence="" of="" silicate,="" the="" bonding="" between="" periclase="" and="" periclase="" will="" be="" strengthened="" by="" cr2o3,="" but="" reduced="" by="" al2o3="" and="" fe2o3.="" the="" higher="" the="" content="" of="" cr2o3,="" the="" more="" intragranular="" and="" intergranular="" spinels,="" the="" higher="" the="" strength="" of="" the="" product="" and="" the="" stronger="" the="" slag="">
직접 결합 된 마그네시아 크롬 벽돌은 일반적으로 낮은 다공성, 고강도, 강한 내마모성, 우수한 내식성 및 우수한 스팔링 저항을 가진 Cr2O3 % ≥ 12 % 및 Cr2O3 ≥ 20 %의 다른 등급으로 나뉩니다. 제품은 전기 아크로, 구리 제련로 및 외부 정제로에서 널리 이용됩니다